SFT-TwistedBundleFiber
For Structural Integrity Maintenance
SFT-TwistedBundleFiber have many advantages thanks to their unique properties. In addition to preventing further expansion of concrete structures and helping maintain the structure integrity, this material can prevent cracks as they are spread throughout the concrete evenly which stops microcracks. Consequently, the structure’s longevity is increased and is less susceptible to natural damages caused by water, electricity and corrosion.
Download Product Sheet
Enter your email address below to download the SFT-TwistedBundleFiber Product Sheet
Data Sheet
Package: 10kg/bag, 10tons/20ft container
| Type I | Type II | |
| Material | 100% Polypropylene | 100% Polypropylene |
| Appearance | Twisted Bundle - Round Fiber | Twisted Bundle - Flat Fiber |
| Dimension | Length 54 mm, 48 mm Thickness 7mm | Length 54 mm, 48 mm Thickness 7mm |
| Color | Grey/Black | Grey/Black |
| Tensile | > 560 MPa | > 560 MPa |
| Elastic Modulus | > 6500 MPa | > 6500 MPa |
| Corrosion | Non-corrosion | Non-corrosion |
| Water Absorption | No | No |
| Acid & Alkali Resistance | Yes | Yes |
| Density | 0.91 - 0.93 g/cm3 | 0.91 - 0.93 g/cm3 |
| Melting Point | 160 - 170 °C | 160 - 170 °C |
| Ignition Point | > 360 °C | > 360 °C |
SFT-WavePPFiber
For Crack Resistance
Polypropylene bundle wave fiber, also known as polypropylene threaded fiber, is made of polypropylene through special parallel drawing and wave forming process and surface treatment. It has the advantages of high cracking strength, good dispersion in concrete, and strong gripping force, and is used for crack resistance enhancement of cement concrete. SFT-WavePPFiber is made of synthetic resin as raw material and processed through special process and surface treatment. Also, it is high alkaline resistant.
Compared to steel fiber, its characteristics are: corrosion resistance, easy dispersion, easy construction and no damage to mixing equipment
Download Product Sheet
Enter your email address below to download the SFT-WavePPFiber Product Sheet
Data Sheet
Packing: regular packing 1.0kg/bag, or according to user’s requirements.
| Size (Width*Length) | Color | Tensile Strength | Gravity (g/cm3) | Melting Point (°C) |
| 0.9 +/- 0.2 mm * 25 mm | Nature/Black | > 400 MPa | 0.91 - 0.95 | 160 - 170 |
| 0.9 +/- 0.2 mm * 36 mm | Nature/Black | > 400 MPa | 0.91 - 0.95 | 160 - 170 |
| 0.9 +/- 0.2 mm * 40 mm | Nature/Black | > 400 MPa | 0.91 - 0.95 | 160 - 170 |
Dosage:
It is recommended to add 3kg per cubic meter of concrete.
Length selection:
Generally, 36mm for anti-cracking reinforcement; when mixed into shotcrete, the length is preferably no more than 25mm. Avoid using gauges larger than 35mm.
Proportion design:
In general, it is not necessary to change the grade and proportion parameters of concrete.
Considering the crack resistance performance requirements of concrete, it can be used in conjunction with adding 0.9 kg of monofilament fiber per square concrete.
Mixer selection:
Choose a double-shaft horizontal forced mixer.
Feeding and Mixing Process
- Put in crushed stone first
- Put in reinforcing ribs, then put in sand
- Stir for 2 minutes to fully disperse the reinforcing ribs
- Put in cement and water and stir evenly according to the conventional process
- It can also be constructed according to the sequence of conventional process input, but the mixing and stirring time should not be less than 4 minutes, and the vibrating time should be extended appropriately to make the fiber fully mixed.